For welding cold work steels, punch dies, cutting dies & shears, piercing form, industrial knives, forming dies, harden surface of work piece. This is a sort of high hardness, grinding-resisted, great toughness Argon filler rod.
CMC-EMagic10
3.2*350mm
CMC EMagic10 is an effective welding rod with knife edge, which containing large percentage of W and Cr. It can achieve low current and high filler rate. Welded melting metal embodies excellent toughness and good impact resistance. After being welded, melting metal is well machinable and has full smoothness, fabulous adhesive property and automatic shell ejecting. It fits for welding of damaged cold-working steel, especially for punching part of large stamping mold. As for cutting tools, they also can get cutting share by welding on low alloy or ordinary steel during producing procedure. And under punching working environment in high speed and high temperature, it still can keep its good impact resistance, especially fitting for mending and welding for damaged mold after its quench hardening. Only one of its layers can get much higher hardness degree. Melting metal can be quenched with SKD11 and still keep high hardness.
CMC-EMagic6
3.2*350mm
CMC EMagic6 is an effective welding rod with knife edge, which can achieve low current and high filler rate. Welded melting metal embodies excellent toughness, good impact resistance, full smoothness, fabulous adhesive property and automatic shell ejecting. CMCEMagic6 is well machinable. And it fits for welding of damaged cold-working steel, especially for punching part of large stamping mold. As for cutting tools, they also can get cutting share by welding on low alloy or ordinary steel during producing procedure.
CMC-SSH
1.6,2.0,2.4
Used for welding directly on High Chromium Cast Iron, cast iron, could be high strength, and good ductility. After welded would be high hardness and easy to polish that could reduce drawing stamp. Applied to cast iron and ductile iron and suitable for machinery processing. Also used for die steel parts such as S45C and steel casting, etc. Enhance their roughness and hardness, mainly used for glass fiber dies, sheet hardware stamping dies.
CMC-ICD5
1.2 1.6 2.4
Welding steel after hardening of air cooling steel, die cutting blade repair, high hardness of argon welding rod.
CMC-Emagic7
3.2*350mm
A common electrode for welding rod of cutting edge can be directly welded to the Cr12MoV steel after heat treatment, the higher the hardness of the performance of specific alkaline coating can reduce the stomatal production; if you watch out the temperature in the pipe, and it does not rise with the increase of welding The lower hardness; In addition, the direct welding of the casting iron and the cast steeling the magic on the welding electrodes, welding adhesion good, starting from Layer 1 can have high hardness. Can fillet welding, welding, flat welding, melting of a high fill rate, can accelerate the efficiency of welding repair, welding on the exchange of fire is relatively terrible.
CMC-E58
2.4 , 3.2 , 4.0
Be suitable for cool working steel damage surfacing, especially for cutting angle and sideline of cold forging die, knife-die, Automotive stamping die, hardware stamping die. For the production of cut tools, also can be surfacing as a shear edge by welding to low-alloy or ordinary steel. Can also be applied to wearing resistance parts hard surface making.
CMC E58 Low Current: 80~110 for 3.2mm Hardness: HRC 57~59
Welding Cold working steel
Repair Cutting edge and Punch die & mould
CMC-12Cr
1.0,1.2 ,1.6,2.4,3.2
Specially used for Cr12!BCr12MoV series mold argon welding wire. If more than three layers need to be welded, CMC-30N can be used as the base. When being used for Cr12 after heat treatment, no need of preheating for small area. The weld hardness is enough, it can be used for mechanical processing.
CMC-Magic1
Very not easy to crack, suitable for high carbon content heat-treated steel. Be used for embossing & drawing die, which can greatly reduce the scratches caused by bending and stretching between high tension steel and ordinary one.
CMC-ECI55
3.2*350mm
Particularly it is suitable for deep drawing mold repair and high R-Angle Drawing hardness of parts produced. Welding directly on the cast iron mold GGG70L, FCD, GM241, etc ... the welding is fine, with very high hardness and wear-resistant, which is easy to be polished. An effective electrode (fill rate of 120% melt) ductile iron, gray cast iron and cast steel flame quenching can also be directly surfacing.
CMC-E46N
2.4 3.2
Used for welding directly on High Chromium Cast Iron, cast iron, high strength, and good ductility. After welded would be high hardness and easy to polish that could reduce drawing stamp. Applied to cast iron and ductile iron and suitable for machinery processing.
Suitable for repairing and joining of High Chromium Cast Iron(GM241)
HRC 45~48
For mending drawbead part of sheet metal press die
CMC-E45
2.6 , 3.2 , 4.0
A kind of middle hard steel welding electrode, be suitable for air cooling steel and cast iron such as ICD5, 7CrSiMinMoV and so on. Applied to welding the drawing parts of vehicle sheet metal covering part die and large hardware sheet metal stamping die, also suitable for hard surface making.
A kind of middle hard steel welding electrode, be suitable for air cooling steel (air hardening materials) and cast iron such as ICD5, 7CrSiMinMoV and So on. Applied to welding the drawing parts of vehicle sheet metal covering part die and large hardware sheet metal stamping Die, also suitable for hard surface making.
CMC-E64N
3.2*350mm
CMC-E64N is suitable for surfacing and joining of all grades of cast iton, high strength, and good ductility. The weld metal could be machinery processing.
Economical Ni-bearing electrodes
Good machining property
Suitable for repair and joining various of cast irons
CMC-ENCD
3.2*350mm
The electrodes can be welding directly on the cast iron and especially for the welding between Mocr cast iron and other cast iron. It is a iron electrode with low rigidity and can be machined after welded. There aren¡¦t any color differences in common cast iron electrodes for its components are very near cast iron. The electrodes can be heated with cast iron after welded. Good welding performance and no gas holes or cracks.
CMC-E62N
3.2*350mm
Special for cast iron die for its lower contain of nickel can reduce cost. The base buffer layer for is made by steel die through hard-face production.
CMC-E60A
2.6 3.2
The electrodes are used for filling mold and high speed steel broach with good welding performance. The electric arc is spraying arc and easy to remove, so it has a smooth and superfine corrugated welding appearance. Molten gold has Characteristics of highly resistant of friction, compression, and strike which is suitable for the production of raw materials, or hot hard-face die with high rigidity with resistant to 500 degrees Celsius.
CMC-E30N
2.6 3.2
Used for joining a broad range of difficult-to-weld metals including special, austenitic-manganese, Air hardening materials for dissimilar-metal joining. Depend on the ferrite content which suitable for designing the joining difficult-to-weld steels, welding of dissimilar joints and rebuilding or buffering before hard surfacing.
Used for joining a broad range of difficult-to-weld metals including special, austenitic-manganese, Air hardening materials for dissimilar-metal joining. Depending on the ferrit content suitable for designed for joining difficult-to-weld steels, welding of dissimilar joints and rebuilding or buffering before hardsurfacing.