TYPE

PATTERN

INSTRUCTION

CMC-EMagic7 *

3.2

A common electrode for welding rod of cutting edge can be directly welded to the Cr12MoV steel after heat treatment, the higher the hardness of the performance of specific alkaline coating can reduce the stomatal production; if you watch out the temperature in the pipe, and it does not rise with the increase of welding The lower hardness; In addition, the direct welding of the casting iron and the cast steeling the magic on the welding electrodes, welding adhesion good, starting from Layer 1 can have high hardness. Can fillet welding, welding, flat welding, melting of a high recovery rate, can accelerate the efficiency of welding repair, welding on the exchange of fire is relatively terrible.

CMC-ECI55 *

3.2

Particularly it is suitable for deep drawing mold repair and high R-Angle Drawing hardness of parts produced. Welding directly on the cast iron mold GGG70L, FCD, GM241, etc ... the welding is fine, with very high hardness and wear-resistant, which is easy to be polished. An effective electrode (effective electrode efficiency of 120% melt) ductile iron, gray cast iron and cast steel flame quenching can also be directly surfacing.

CMC-E46H *

3.2

Especially suitable for R-Mo angle of chromium cast iron mold drawing parts repair and production. Melting gold detailed, which is easy to prevent the sheet metal parts polishing scratches; hardness is in a high level, and suitable for demanding draw bead manufacturing. Ductile iron, gray cast iron and cast steel flame quenching can also be directly surfacing.

CMC-ENCD *

2.5 3.2

It can be applied directly on the cast iron welding, especially for MoCr cast iron with a variety of cast iron welding repair. Iron base is for a low hardness cast iron welding rod, weld can be processed, and because the composition is very close with the cast iron, cast iron welding rod so I do not have general problems of chromatic aberration, and after welding, heat treatment can be accompanied by cast iron. Good welding is in good performance, no air holes and cracks.

CMC-EH10 *

3.2 4.0

It is applicable to the large-scale production of hot hammer forging dies, repairing and surface reconstruction. Because of the reduction of the chromium content, it forms the high temperature wear and toughness, good balance, a substantial increase in cross-sectional area larger hot die life. Widely used in the large hot hammer forging dies thermal gravity die casting mold and the wear parts of hard surface is made.

CMC-FC864Mo *

1.6

New Tubular Cr-Mo alloyed metalcored wire can be suitable for all kinds of hot work die steel welding and repair welding of reconstruction, especially for the initial hot forging die, die forging an important block in the strengthening of the local armor type welding. For the eager mode of production, can also be produced by welding knife. As Mo, Cr content is high, there are very good in high-temperature hardness and heat conductivity.

CMC-FC867 *

1.6

Tubular basic flux cored wire is suitable for all kinds of hot work die steel and it is filled with welding repair and reconstruction, Especially for the initial hot forging die forging, die forging an important block in the strengthening of the local armor-type welding. After welding, it does not need to harden the heat treatment, which can be used directly, without softening annealing process, it can be machined directly on the main processing machine. As the Mo content was high, with very good thermal conductivity and heat resistance to abrasion.

CMC-FC815 *

1.6

New-type metal power bonding wire is suitable for all kinds of hot forging dies, heat-resistant ceramic molds, wear parts production and welding repair. It also can be used in carbon steel and low alloy steel to enhance the surface hardness. After welding, welds do not need to hardening heat treatment can be used directly and processed.

CMC-M3-5 *

3.6

Co series of high-speed steel is suitable for all kinds of hot shear modulus, thermal die, hot punch the work environment; excellent high temperature strength, anti-wearing and impact resistance. Heat load is applied to the thermal resistance welding repair tools and hard surface for the high hardness of production of argon welding rod.

CMC-ICD5 *

1.2 1.6

2.4 3.2

Welding steel after hardening of air cooling steel, die cutting blade repair, high hardness of argon welding rod.

CMC-2365

1.6

Hot Copper and Aluminum Forging Die Welding, copper and aluminum die casting mold, with excellent heat resistance, wear resistance, cracking sound argon welding rod.